聚醚醚酮,膜, PEEK, 0.038mm厚
半岛bd体育手机客户端 介绍
订货号 |
包装规格 |
Sizes |
013-075-40 |
150 mm x 150 mm |
002-226-57 |
300 mm x 300 mm |
757-280-21 |
600 mm x 600 mm |
Coil |
322-600-70 |
1 m |
584-809-71 |
2 m |
825-657-58 |
5 m |
089-412-71 |
10 m |
半岛bd体育手机客户端 参数
Coil Width[卷材宽度] |
650mm |
Grade[等级] |
VICTREX? APTIV? 2000 |
Structure[结构] |
Amorphous |
Surface Finish[表面光洁度] |
Matt/Gloss |
Thickness[厚度] |
0.038mm |
Transparency[透明度] |
Transparent Pale Amber |
Chemical Resistance(耐化学性) |
Acids - concentrated |
Good-Poor |
Acids - dilute |
Good |
Alcohols |
Good |
Alkalis |
Good |
Aromatic hydrocarbons |
Good |
Greases and Oils |
Good |
Halogenated Hydrocarbons |
Good |
Halogens |
Good-Poor |
Ketones |
Good-Poor |
Thermal Properties(热性能) |
Coefficient of thermal expansion ( x10?? K?? ) |
47.000 - 108.000 |
Heat-deflection temperature - 0.45MPa ( C ) |
> 260 |
Heat-deflection temperature - 1.8MPa ( C ) |
160.0 |
Specific heat ( J K?? kg?? ) |
1340.0 |
Thermal conductivity ( W m?? K?? ) |
0.25 @23℃ |
Upper working temperature ( C ) |
250 |
Physical Properties(物理性质) |
Density ( g cm?? ) |
1.260 - 1.320 |
Flammability |
V-0@1.5mm |
Limiting oxygen index ( % ) |
35 |
Radiation resistance |
Good |
Resistance to Ultra-violet |
Fair |
Water absorption - equilibrium ( % ) |
0.50 |
Water absorption - over 24 hours ( % ) |
0.100 - 0.300 |
Mechanical Properties(机械性能) |
Coefficient of friction |
0.18 |
Elongation at break ( % ) |
50.0 |
Hardness - Rockwell |
M99 |
Izod impact strength ( J m?? ) |
85.0 |
Poisson's ratio |
0.400 |
Tensile modulus ( GPa ) |
3.70 - 4.00 |
Tensile strength ( MPa ) |
70.00 - 100.00 |
Electrical Properties(电气特性) |
Dielectric constant @1kHz |
3.20 - 3.30 @50Hz-10Khz |
Dielectric strength ( kV mm?? ) |
190.0 @50μm |
Dissipation factor @ 1MHz |
0.0030 |
Volume resistivity ( Ohmcm ) |
10??-10?? |
其他参数
公差
直径 |
<100mm |
±1mm |
≥100mm |
+2% / -1% |
厚度 |
|
±20% |
长度 1 |
<100mm |
±1mm |
≥100mm |
+2% / -1% |
长度 2 |
<100mm |
±1mm |
≥100mm |
+2% / -1% |
|
|
Goodfellow(顾特服)
电话:点击&查看18024074014
地址: