The Honeycomb is made from Aluminium alloy foil which is chemically treated, node bonded and expanded to form a low density material used principally as a shear-carrying-core in lightweight sandwich constructions.

We stock both honeycomb core and skinned lightweight sandwich panels made using some of these cores.

The typical properties of the honeycomb cores stocked which are all made from 5052 Aluminium alloy are shown in the data table.

Other densities, cell sizes and core and foil thicknesses available on request.

Flat, ready-made honeycomb sandwich panels. Aluminium core with Carbon Fibre / Epoxy composite facing skins (fibre orientation 0/90). Thickness includes facing skins.

订货号	包装规格
Sizes
639-704-98	300mm x 300mm
963-123-26	600mm x 600mm

半岛bd体育手机客户端 参数

Adhesive[胶粘剂]	Phenolic
Cell Size[空穴大小]	6.3mm
Cell Wall[空穴壁厚]	0.064mm
Core Density[堆芯密度]	0.083g.cm??
Facing Skin[面料]	Carbon Fibre / Epoxy
Thickness[厚度]	26.5mm
Atomic Properties(原子属性)
Atomic number	13
Atomic weight ( amu )	26.98154
Crystal structure	Face Centred Cubic
Electronic structure	Ne3s?3p?
Ionisation potential ( No./eV )	4 / 120
Ionisation potential ( No./eV )	5 / 154
Ionisation potential ( No./eV )	6 / 190
Ionisation potential ( No./eV )	1 / 5.99
Ionisation potential ( No./eV )	3 / 28.4
Ionisation potential ( No./eV )	2 / 18.8
Photo-electric work function ( eV )	4.20
Thermal neutron absorption cross-section ( Barns )	0.2320
Valences shown	3
Electrical Properties(电气特性)
Electrical resistivity ( μOhmcm )	2.67@20℃
Superconductivity critical temperature ( K )	1.1750
Temperature coefficient ( K?? )	0.00450 @0-100℃
Thermal emf against Pt (cold 0C - hot 100C) ( mV )	0.42
Mechanical Properties(机械性能)
Bulk modulus ( GPa ) ( Hard )	75.2
Bulk modulus ( GPa ) ( Soft )	75.2
Hardness - Vickers ( kgf mm?? ) ( Hard )	35 - 48
Hardness - Vickers ( kgf mm?? ) ( Soft )	21
Material condition	Soft
Material condition	Hard
Poisson's ratio ( Hard )	0.345
Poisson's ratio ( Soft )	0.345
Tensile modulus ( GPa ) ( Hard )	70.60
Tensile modulus ( GPa ) ( Soft )	70.60
Tensile strength ( MPa ) ( Hard )	130.00 - 195.00
Tensile strength ( MPa ) ( Soft )	50.00 - 90.00
Yield strength ( MPa ) ( Hard )	110.0 - 170.0
Yield strength ( MPa ) ( Soft )	10.0 - 35.0
Physical Properties(物理性质)
Boiling point ( C )	2467
Density ( g cm?? )	2.700 @20℃
Thermal Properties(热性能)
Coefficient of thermal expansion ( x10?? K?? )	23.500 @0-100℃
Latent heat of evaporation ( J g?? )	10800
Latent heat of fusion ( J g?? )	388.00
Melting point ( C )	660.40
Specific heat ( J K?? kg?? )	900.0 @25℃
Thermal conductivity ( W m?? K?? )	237.00 @0-100℃