Purity[纯度] |
99.9% |
Surface Finish[表面光洁度] |
Polished On Both Sides |
Temper[状态] |
As Rolled |
Thickness[厚度] |
1mm |
Typical Analysis(典型分析) |
Al |
70 PPM |
Cu |
20 PPM |
Fe |
280 PPM |
Mn |
170 PPM |
Ni |
<10 PPM |
Si |
50 PPM |
Zn |
<20 PPM |
Thermal Properties(热性能) |
Coefficient of thermal expansion ( x10?? K?? ) |
26.000 @0-100℃ |
Latent heat of evaporation ( J g?? ) |
5254 |
Latent heat of fusion ( J g?? ) |
362.00 |
Melting point ( C ) |
649.00 |
Specific heat ( J K?? kg?? ) |
1020.0 @25℃ |
Thermal conductivity ( W m?? K?? ) |
156.00 @0-100℃ |
Mechanical Properties(机械性能) |
Bulk modulus ( GPa ) ( Hard ) |
35.6 |
Bulk modulus ( GPa ) ( Soft ) |
35.6 |
Hardness - Vickers ( kgf mm?? ) ( Hard ) |
35 - 45 |
Hardness - Vickers ( kgf mm?? ) ( Soft ) |
30 - 35 |
Material condition |
Hard |
Material condition |
Soft |
Poisson's ratio ( Hard ) |
0.291 |
Poisson's ratio ( Soft ) |
0.291 |
Tensile modulus ( GPa ) ( Hard ) |
44.70 |
Tensile modulus ( GPa ) ( Soft ) |
44.70 |
Tensile strength ( MPa ) ( Hard ) |
232.00 |
Tensile strength ( MPa ) ( Soft ) |
185.00 |
Yield strength ( MPa ) ( Hard ) |
100.0 |
Yield strength ( MPa ) ( Soft ) |
69.0 |
Atomic Properties(原子属性) |
Atomic number |
12 |
Atomic weight ( amu ) |
24.30500 |
Crystal structure |
Hexagonal Close Packed |
Electronic structure |
Ne3s? |
Ionisation potential ( No./eV ) |
2 / 15.03 |
Ionisation potential ( No./eV ) |
6 / 187 |
Ionisation potential ( No./eV ) |
4 / 109 |
Ionisation potential ( No./eV ) |
5 / 141 |
Ionisation potential ( No./eV ) |
1 / 7.65 |
Ionisation potential ( No./eV ) |
3 / 80.1 |
Natural isotope distribution ( Mass No./% ) |
24 / 78.99 |
Natural isotope distribution ( Mass No./% ) |
26 / 11.01 |
Natural isotope distribution ( Mass No./% ) |
25 / 10.00 |
Photo-electric work function ( eV ) |
3.66 |
Thermal neutron absorption cross-section ( Barns ) |
0.0640 |
Valences shown |
2 |
Physical Properties(物理性质) |
Boiling point ( C ) |
1090 |
Density ( g cm?? ) |
1.740 @20℃ |
Electrical Properties(电气特性) |
Electrical resistivity ( μOhmcm ) |
4.2@20℃ |
Temperature coefficient ( K?? ) |
0.00425 @0-100℃ |
Thermal emf against Pt (cold 0C - hot 100C) ( mV ) |
0.44 |