材料 >> 聚合物材料
氟化乙烯丙烯共聚物,膜, FEP, 0.05mm厚
半岛bd体育手机客户端 介绍
| 订货号 |
包装规格 |
| Sizes |
| 298-646-49 |
150 mm x 150 mm |
| 330-801-83 |
300 mm x 300 mm |
| Coil |
| 350-225-63 |
0.5 m |
| 778-205-65 |
1 m |
| 275-707-42 |
2 m |
| 588-013-50 |
5 m |
| 889-726-88 |
10 m |
| 537-517-86 |
20 m |
半岛bd体育手机客户端 参数
| Coil Width[卷材宽度] |
610mm |
| Thickness[厚度] |
0.05mm |
| Transparency[透明度] |
Clear/Transparent |
| Mechanical Properties(机械性能) |
| Coefficient of friction |
0.27 - 0.67 |
| Elongation at break ( % ) |
150.0 -300.0 |
| Hardness - Rockwell |
R25-45,60 Shore D |
| Izod impact strength ( J m?? ) |
999999.0 - No Break |
| Poisson's ratio |
0.480 |
| Tensile modulus ( GPa ) |
0.50 - 0.60 |
| Tensile strength ( MPa ) |
14.00 - 30.00 |
| Physical Properties(物理性质) |
| Density ( g cm?? ) |
2.150 |
| Flammability |
V-0 |
| Limiting oxygen index ( % ) |
95 |
| Radiation resistance |
Poor |
| Refractive index |
1.344 |
| Resistance to Ultra-violet |
Excellent |
| Water absorption ( % ) |
0.01 |
| Electrical Properties(电气特性) |
| Dielectric constant @1MHz |
2 |
| Dielectric strength ( kV mm?? ) |
20.0 @3.2mm |
| Dissipation factor @ 1MHz |
0.0007 |
| Surface resistivity ( Ohm/sq ) |
10?? |
| Volume resistivity ( Ohmcm ) |
10?? |
| Thermal Properties(热性能) |
| Coefficient of thermal expansion ( x10?? K?? ) |
83.000 - 104.000 |
| Heat-deflection temperature - 0.45MPa ( C ) |
50 |
| Heat-deflection temperature - 1.8MPa ( C ) |
70.0 |
| Lower working temperature ( C ) |
-250 |
| Specific heat ( J K?? kg?? ) |
1100.0 |
| Thermal conductivity ( W m?? K?? ) |
0.19 - 0.24 @23℃ |
| Upper working temperature ( C ) |
150 - 200 |
| Chemical Resistance(耐化学性) |
| Acids - concentrated |
Good |
| Acids - dilute |
Good |
| Alcohols |
Good |
| Alkalis |
Good |
| Aromatic hydrocarbons |
Good |
| Greases and Oils |
Good |
| Halogenated Hydrocarbons |
Good |
| Halogens |
Good |
| Ketones |
Good |
其他参数
公差
| 直径 |
<100mm |
±1mm |
| ≥100mm |
+2% / -1% |
| 厚度 |
|
±20% |
| 长度 1 |
<100mm |
±1mm |
| ≥100mm |
+2% / -1% |
| 长度 2 |
<100mm |
±1mm |
| ≥100mm |
+2% / -1% |
|
|
相关半岛bd体育手机客户端
|