Aluminium foam is produced from 6101 Aluminium alloy, retaining 99% purity of the parent alloy. It has a reticulated structure; the cells are open and have a duodecahedral shape. The unique mechanical properties of Aluminium foam are high surface area to volume, high strength to weight ratio and a completely isotropic load response. The foam has many of the properties of the alloy, such as corosion resistance, srength, electrical and thermal conductivity, but at a fraction of the weight.
| 订货号 |
包装规格 |
| Sizes |
| 373-062-67 |
150mm x 150mm |
半岛bd体育手机客户端 参数
| Bulk Density[容积密度] |
0.2g.cm?3 |
| Grade[等级] |
Aluminium 6101 |
| Pores/cm[孔隙/厘米] |
2 |
| Porosity[孔隙度] |
93% |
| Purity[纯度] |
98.5% |
| Thickness[厚度] |
6.35mm |
| Typical Analysis(典型分析) |
| B |
<0.06 Percent |
| Cr |
<0.03 Percent |
| Cu |
<0.1 Percent |
| Fe |
<0.5 Percent |
| Mg |
0.35 - 0.8 Percent |
| Mn |
<0.03 Percent |
| Si |
0.3 - 0.7 Percent |
| Zn |
<0.1 Percent |
| Atomic Properties(原子属性) |
| Atomic number |
13 |
| Atomic weight ( amu ) |
26.98154 |
| Crystal structure |
Face Centred Cubic |
| Electronic structure |
Ne3s23p1 |
| Ionisation potential ( No./eV ) |
4 / 120 |
| Ionisation potential ( No./eV ) |
5 / 154 |
| Ionisation potential ( No./eV ) |
6 / 190 |
| Ionisation potential ( No./eV ) |
1 / 5.99 |
| Ionisation potential ( No./eV ) |
3 / 28.4 |
| Ionisation potential ( No./eV ) |
2 / 18.8 |
| Photo-electric work function ( eV ) |
4.20 |
| Thermal neutron absorption cross-section ( Barns ) |
0.2320 |
| Valences shown |
3 |
| Electrical Properties(电气特性) |
| Electrical resistivity ( μOhmcm ) |
2.67@20℃ |
| Superconductivity critical temperature ( K ) |
1.1750 |
| Temperature coefficient ( K?1 ) |
0.00450 @0-100℃ |
| Thermal emf against Pt (cold 0C - hot 100C) ( mV ) |
0.42 |
| Mechanical Properties(机械性能) |
| Bulk modulus ( GPa ) ( Hard ) |
75.2 |
| Bulk modulus ( GPa ) ( Soft ) |
75.2 |
| Hardness - Vickers ( kgf mm?2 ) ( Hard ) |
35 - 48 |
| Hardness - Vickers ( kgf mm?2 ) ( Soft ) |
21 |
| Material condition |
Soft |
| Material condition |
Hard |
| Poisson's ratio ( Hard ) |
0.345 |
| Poisson's ratio ( Soft ) |
0.345 |
| Tensile modulus ( GPa ) ( Hard ) |
70.60 |
| Tensile modulus ( GPa ) ( Soft ) |
70.60 |
| Tensile strength ( MPa ) ( Hard ) |
130.00 - 195.00 |
| Tensile strength ( MPa ) ( Soft ) |
50.00 - 90.00 |
| Yield strength ( MPa ) ( Hard ) |
110.0 - 170.0 |
| Yield strength ( MPa ) ( Soft ) |
10.0 - 35.0 |
| Physical Properties(物理性质) |
| Boiling point ( C ) |
2467 |
| Density ( g cm?3 ) |
2.700 @20℃ |
| Thermal Properties(热性能) |
| Coefficient of thermal expansion ( x10?? K?1 ) |
23.500 @0-100℃ |
| Latent heat of evaporation ( J g?1 ) |
10800 |
| Latent heat of fusion ( J g?1 ) |
388.00 |
| Melting point ( C ) |
660.40 |
| Specific heat ( J K?1 kg?1 ) |
900.0 @25℃ |
| Thermal conductivity ( W m?1 K?1 ) |
237.00 @0-100℃ |